Basalt fire-resistant roll material (MBOR)

Basalt fire-resistant roll material is a stitched canvas made of basalt super-thin fibers without binder

more
thumbnail MBOR (Basalt fire-resistant roll material) is a stitched canvas made of basalt super-thin fibers without binder, with or without coating.

MBOR-5, 8, 10, 13, 16 - uncoated material

MBOR-5Ф, 8Ф, 10Ф, 13Ф, 16Ф, 18Ф, 20Ф, 23Ф, 26Ф  - aluminum foil coated material

MBOR-С-5, 8, 10, 13, 16, 18, 20 - material with fiberglass coating on one side

MBOR-С2-5, 8, 10, 13, 16, 18, 20 - material with fiberglass coating on both sides 

Technical parameters

Flammability group
non-combustible
Application temperature
-200...+900 °С
Density, kg/m3
100 ±10%
Thermal Conductivity in 25 °C, λ25
0,033 W/m*K
Thermal Conductivity in 125 °C, λ125
0,051 W/m*K
Thermal Conductivity in 300 °C, λ300
0,09 W/m*K

STITCHED MATS FROM STAPLE FIBER (TIB)

TIB-stitched products made of staple basalt superfine fiber without a cover material or with a coating of fiberglass, basalt or silica fabric, stitched with threads.

more
thumbnail TIB - stitched products from staple basalt superfine fiber without cover material, stitched with threads. Application temperature – from -260°С to +700°С

ТИБ-1С,2С,6С - Coated with glass fiber. Application temperature – from -260°С to +400°С

ТИБ-1Б,2Б,6Б - Covered with basalt fabric. Application temperature – from -260°С to +600°С

ТИБ-1К,2К,6К - Coated with silica fabric. Application temperature – from -260°С to +700°С

Used for thermal insulation of industrial equipment and pipelines, ship premises, power and other ship equipment, nuclear power plant equipment.

Technical parameters

Density, kg / m3, no more
23
Thermal conductivity at 298 K, W / m * K, no more
0,038
Application temperature TIB-1C, 2C, 6C
от -260°С до +400°С
Application temperature TIB-1B, 2B, 6B
от -260°С до +600°С
Application temperature TIB-1K, 2K, 6K
от -260°С до +700°С

HEAT AND SOUND INSULATING MATERIAL ATM-3

Heat and sound insulation material ATM-3 consists of a loose layer of super-thin staple glass fiber bonded with synthetic resin, lined from both sides with glass fabric and stitched with threads.

more
thumbnail Heat and sound insulation material ATM-3 consists of a loose layer of super-thin staple glass fiber bonded with synthetic resin, lined from both sides with glass fabric and stitched with threads.

ATM-3 is used for heat and sound insulation of industrial equipment, aircraft building, spacecraft compartments, orbital stations, automobile, railway and water transport, in industrial and civil construction.

Technical parameters

Length, mm
1100
Width, mm
600
Thickness, mm
10, 15, 20, 30
Humidity,%, no more
2
Density, kg/m3
40-70

Heat and noise insulating material ATM-10

Heat and sound insulating mats ATM-10 is made from basalt staple superthin fiber covered fully with glass or silica fabric and stitched with corresponding threads.

more
thumbnail Heat and sound insulating mats ATM-10 is made from basalt staple superthin fiber covered fully with glass or silica fabric and stitched with corresponding threads.

Heat and sound insulating mats ATM-10 is used asheat and sound insulating material for industrial equipment, reinforcement and different vehicles as well as in building constructions, aircrafting and ship building.

Mats are non-combustible soundproof materials. The operating temperature range is:
  • from -200°С to +450°С – For mats with a glass fabric covered (ATM-10s)
  • from -200°С to +700°С – For mats with a silica fabric covered (ATM-10k)

Technical parameters

Thermal conductivity, at 25°С, W/m*K
0,037
Humidity, % by weight, not more than
2,0
Maximum operating temperature ATM-10s, ° С, не более
450
Maximum operating temperature ATM-10k, °C
700